We are manufacturing high quality carbon electrode paste which is a self baking electrode used in electric or submerged are furnace for delivering power to the change mix. Carbon Electrode Paste is a mix of electrically calcined anthracite or CPC with coal tar pitch and other additional material.
Carbon Electrode Paste is a self-baking electrode used in submerged arc furnaces.
Electrode paste is a soderberg paste, also called self-baking electrodes. It is mainly used as carbon electrodes in electric arc furnace, which is for the production of various types of ferrous and non-ferrous alloys.
Soderberg-type electrode paste is produced from calcined petroleum coke (or calcined pitch coke), calcined anthracite, coal tar pitch and other additional materials.
Introduction
The petroleum coke and the asphalt are dehydrated and melted in the melting tank, and are mixed into a kneading pot in proportion, and then calcined. It has the characteristics of low resistance and is used as a conductive material in electric furnace equipment such as iron alloy furnace and calcium carbide furnace. Electrode paste can be said to be a simple and technically- complicated product in carbon production. After being kneaded and molded, the electrode paste became a finished product. Unlike other carbon and graphite products, when defects occur in the previous process, it can be compensated by baking, graphitization or even an impregnation process. The electrode paste is calcined by the heat in the submerged arc furnace. Therefore, the consumption speed of the electrode and the calcination speed are the key to the use of the electrode paste.
As the ore furnace technology gradually develops toward large-scale and air-tightness, the electrode develops from the open furnace type to the closed furnace type during the calcining process, and the heat obtained by the electrode from the furnace is greatly reduced, which requires an increase in the sintering properties of the electrode paste to compensate for this deficiency.
Technical Specs of Energy-Saving Self-baking Eleclrode for ore-smelting electric furnace
| Item | EP-01 | EP-02 | EP-03 | EP-04 | EP-05 | EP-06 | EP-07 | EP-08 |
| Ash Content (%) | ≤3.0 | ≤3.5 | ≤4.0 | ≤4.5 | ≤5.0 | ≤6.0 | ≤6.5 | ≤7.0 |
| Volatile (%) | 9-15 | 9-15 | 9-15 | 9-15 | 9-15 | 9-15 | 9-15 | 9-15 |
| Compressive Strength (Mpa) | ≥19 | ≥20 | ≥21 | ≥22 | ≥22 | ≥23 | ≥23 | ≥23 |
| Resistivity (μΩ.m) | ≤63 | ≤64 | ≤65 | ≤70 | ≤73 | ≤75 | ≤78 | ≤80 |
| Bulk Density (g/cm³) | ≥1.4 | ≥1.4 | ≥1.4 | ≥1.38 | ≥I .38 | ≥1.38 | ≥1.38 | ≥1.38 |
Regular Specs for Metallurgical Industry
| Si | <0.28% | Fe | <0.25% |
| P | 0.004% | ||
| Ash content | 2-10% | Resistivity | 55-90 uOm |
| V.M | 10.0-15.0% | Density | >1.46g/cm3 |
| Compression Strength | >18Mpa | Extensibility | 6-20 |
| Apparent Density | >1.42g/cm3 | Rupture Density | >4.0 |
| Real Density | >1.98g/cm3 | Fluidity coefficient | 1.10-2.10 |